Fluoroplastic FEP Resin,FEP,FEP Pellet,Everflon

Get to know Everflon™ FEP 4630HT.

Everflonultra™ FEP 4630HT is a melt-processible fluoroplastic resin available in pellet form. It is a copolymer of tetrafluoroethylene, hexafluoropropylene and ppve,without additives, that meets the requirements of ASTM D 2116 Type II. With a relatively high melt flow rate and improved high frequency electrical properties,Everflonultra™ FEP 4630HT has been designed for high-speed extrusion of thin coatings on small-gauge wires.

Everflonultra™ FEP 4630HT has a higher melt flow rate than most other fluoroplastic resins. This permits higher extrusion speeds and easier processing, making Everflonultra™ FEP 4630HT a cost-effective alternative for producing thin-wall extrusions.

Everflonultra™ FEP 4630HT is designed and made to have improved dissipation factor at high frequencies, and to have significant plate-out resistance in melt extrusion.It is suitable as a solid insulator and as a foamed insulator when used with an appropriate nucleant in a nitrogen gas injection process.

Everflonultra™ FEP 4630HT is used when traditional extrusion and molding processes are required for producing products with the superior properties of a fluoroplastic resin. Compared to other thermoplastics, the high melt strength and thermal stability of Everflonultra™ FEP 4630HT can be used to improve processing rates. Compared with other fluoroplastics, creep resistance at high service temperatures provides a superior balance and level of end-use properties. Everflonultra™ FEP 4630HT combines the processing ease of conventional thermoplastics with many properties similar to those of PFA.

Properly processed products made from neat Everflonultra™ FEP 4630HT resin provide the superior properties characteristic of fluoroplastic resins: chemical inertness, exceptional dielectric properties, heat resistance, toughness and flexibility,low coefficient of friction, nonstick characteristics, negligible moisture absorption, low flammability, performance at temperature extremes, and excellent weather resistance.In a flame situation, products of Everflonultra™ FEP 4630HT resist ignition and do not promote flame spread. When ignited by flame from other sources, their contribution of heat is very small and added at a slow rate with very little smoke.

Typical Applications

Applications for Everflonultra™ FEP 4630HT include small diameter, thin wall wire and cable insulation; industrial film; and intricate or thin wall parts made by injection molding.

Processing Guide

Everflonultra™ FEP fluoroplastic resin can be processed by conventional melt extrusion, and by injection, com-pression, and blow molding processes.

For smooth feeding to extrusion equipment, it is supplied in 3 mm (0.12 in) pellets.

The extruders and molding machines used for Everflon™ FEP should be constructed of high nickel alloy corro-sion-resistant materials and be capable of operating at temperatures up to 400 °C (750 °F)

Precaution

Industrial experience has proven that adequate ventilation, in properly maintained processing and handling areas, will eliminate known hazards to personnel. Resin containers should be opened and used in well-ventilated areas.

Equipment used to process at melt temperatures should be provided with local exhaust ventilation (LEV) to com-pletely remove all fumes and vapors from the processing area. In addition, care should be exercised to avoid the contamination of cigarettes and other forms of smoking tobacco when using fluoroplastic resins.

Before processing any fluoroplastics, read the Material Safety Data Sheet, available upon request from our Cus-tomer Service Group. Also read the detailed information in the latest edition of the “Guide to the Safe Handling of Fluoropolymer Resins”.

Handling & Packing

Everflonultra™ FEP 4630HT is packaged in 25-kg, single layer, plastic bags. For convenient shipment, orders of 1000-kg gallary are recommended. The properties of Everflon™ FEP resin are not affected by storage time. Ambient storage conditions should be designed to avoid airborne contamination and water condensation on the resin when it is removed from containers.

Data List

Item	Test Method	Unit	Typical Value
GENERAL
MFI	ASTM D2116	g/10min 372°C 5kg	27~33
Specific Gravity	ASTM D792		2.15
Critical Shear Rate, 372 °C (702 °F)		1/s	200
Guide DDR Range for Jacket Extrusion			60–120
MECHANICAL
Tensile Strength	ASTM D638	Mpa	25
Elongation at Break	ASTM D638	%	350
Impact Strength, Notched Izod, 23 °C (73 °F)	ASTM D256	kJ/m²	No Break
MIT Folding Endurance (0.20 mm, 8 mil film)	ASTM D2176	Cycles	100,000
Hardness Durometer	ISO 868 / ASTM D2240		D56
ELECTRICAL
Dielectric Strength, Short Time, 0.25 mm (0.010 in)	IEC 243 / ASTM D149	kV/mm	> 100
Relative Permittivity, 1 kHz	IEC 250 / ASTM D150		2.03
Relative Permittivity, 1 GHz	IEC 250 / ASTM D150		2.03
Dissipation Factor, tg δ, 1 kHz	ISO 1325 / ASTM D150		0.00005
Dissipation Factor, tg δ, 1 GHz	ISO 1325 / ASTM D150		0.0007
OTHER
Water Absorption, 24 hr	ASTM D570	%	<0.01
Weather and Chemical Resistance			Excellent
Limiting Oxygen Index	ISO 4589 / ASTM D2863	%	> 95
Continuous Service Temperature		°C	240
Flammability Classification	UL 94		V-0