PVDF 203
Get to know Everflon™ PVDF V203.
EverlonTM V203 PVDF homopolymer has very high viscosity, suitable for membrane manufacturing. It is available exclusively as powder.
Precaution
Equipment used to process at melt temperatures should be provided with local exhaust ventilation (LEV) to completely remove all fumes and vapors from the processing area. In addition, care should be exercised to avoid the contamination of cigarettes and other forms of smoking tobacco when using fluoroplastic resins. Before processing any fluoroplastics, read the Material Safety Data Sheet.
Data List
| Property | Test Method | Unit | Typical Value |
| Physical | |||
| Specific Gravity | ASTM D792 | 1.75-1.77 | |
| Water Absorption | ASTM D570 | % | 0.040 |
| MeltMass-FlowRate(MFR)(230°C/21.6kg) | g/10min | <2.0 | |
| Mechanical | |||
| Tensile Modulus(23°C,2.00mm) | ASTMD638 | 2100 to 2300 | |
| Tensile Strength | ASTMD638 | ||
| Yield,23°C,2.00mm | Mpa | 53.0 to 57.0 | |
| Break,23°C,2.00mm | Mpa | 25.0 to 50.0 | |
| Tensile Elogation | ASTMD638 | ||
| Yield,23°C,2.00mm | % | 5.0 to10 | |
| Break,23°C,2.00mm | % | 15 to 50 | |
| Thermal | |||
| MeltingTemperature | ASTM D3418 | ℃ | 171-175 |
| GlassTransitionTemperature | ASTM D4065 | ℃ | -40.0 |
| PeakCrystallizationTemperature(DSC) | ASTM D3418 | ℃ | 133 to 138 |
| CrystallizationHeat | ASTM D3417 | J/g | 47.0 to 52.0 |
| HeatofFusion | ASTM D3417 | J/g | 57.0 to 66.0 |
| Electrical | |||
| SurfaceResistivity | ASTM D257 | ohms | >1.0E+14 |
| VolumeResistivity | ASTM D257 | ohms:cm | >1.0E+14 |